Technical Data Sheet
Catalyst Bed Support Media: Alpha Alumina Spheres
These products are formulated with high purity Alpha Alumina with low silica content to prevent silica leaching and coating on downstream equipment.
CBS-99B has higher density and lower porosity than CBS-99A, so CBS-99B maybe be used on top of catalyst bed to prevent bed lifting, as well as to help insure uniform gas and/or liquid flowover the active catalyst bed.
Chemical Composition
SiO2 |
Al2O3 |
Fe2O3 |
MgO |
CaO |
K2 |
TiO2 |
Na2O |
0.14% |
>99% |
0.05% |
0.001% |
0.001% |
0.04% |
0.017% |
0.390% |
Physical Properties
CBS — 99B
| Item |
Value |
Size |
Crush Strength |
| |
kg/particle |
kN/particle |
| Water Absorption |
<1% |
1/8" (3mm) |
>203 |
>2 |
| Packing Density, kg/m31000 |
1.9 — 2.2 |
1/4" (6mm) |
>459 |
>4.6 |
| Specific Gravity |
>3.6 |
1/2" (13mm) |
>877 |
>8.7 |
| Maximum Operation Temperature °C |
1650 |
3/4" (19mm) |
>1220 |
>12 |
| Apparent porosity, % |
<1 |
1" (25mm) |
>1630 |
>16 |
|
1.5" (38mm) |
>2340 |
>23 |
CBS — 99A
| Item |
Value |
Size |
Crush Strength |
| |
kg/particle |
kN/particle |
| Water Absorption |
<5% |
1/8" (3mm) |
>203 |
>2 |
| Packing Density, kg/m31000 |
1.8 — 2.0 |
1/4" (6mm) |
>459 |
>4.6 |
| Specific Gravity |
3.0 — 3.5 |
1/2" (13mm) |
>877 |
>8.7 |
| Maximum Operation Temperature °C |
1600 |
3/4" (19mm) |
>1220 |
>12 |
| Apparent porosity, % |
<5% |
1" (25mm) |
>1630 |
>16 |
|
1.5" (38mm) |
>2340 |
>23 |
Contact us for more information...
|
|